DF350A Modified Diphenyl Ather Glass panno rigidum laminated sheet
DFCCCLAConsistit ex texta vitream vestimento impraegnated cum immutatus diphenyl Aether thermosetting resinae, laminated sub altum temperatus et pressura. In texi vitrum pannum erit alkali libero et tractata per KH560.
DF350A haberet bonum calor resistentia, optimum mechanica et dielectric possessiones, idoneam applications in H-genus electrica motoribus vel electrica apparatu sicut in Structural partes vel components. Praesertim in his electrica motoribus et electrica apparatu, quae requirere altiorem mechanica operibus sub scelerisque statum accentus.
Available crassitudine:0.5mm ~ 200mm
Available sheet Size:
1500mm * 3000mm, 1220mm * 3000mm, 1020mm * 2040mm, 1220mm * 2440mm, 1000mm * 2000mm et alia agitari magnitudinum.
Et nomina crassitudine et permisit tolerantia (mm)
| Crassitudo nomina | Deviatio | Crassitudo nomina | Deviatio | Crassitudo nomina | Deviatio |
| 0,5 | +/- 0.15 | 3 | +/- 0,37 | 16 | +/- 1.12 |
| 0.6 | +/- 0.15 | 4 | +/- 0.45 | 20 | +/- 1.30 |
| 0,8 | +/- 0.18 | 5 | +/- 0.52 | 25 | +/- 1.50 |
| 1 | +/- 0.18 | 6 | +/- 0.60 | 30 | +/- 1.70 |
| 1.2 | +/- 0,21 | 8 | +/- 0,72 | 35 | +/- 1.95 |
| 1.5 | +/- 0,25 | 10 | +/- 0.94 | 40 | +/- 2,10 |
| 2 | +/- 0,30 | 12 | +/- 0.94 | 45 | +/- 2,45 |
| 2.5 | +/- 0,33 | 14 | +/- 1.02 | 50 | +/- 2.60 |
Flexiones deflectionis (mm)
| Crassities | Tendentes deflectionem | |
| M (princeps longitudinem) | D (princeps longitudinem) | |
| 3.0 ~ 6.0 | ≤10 | ≤2.5 |
| 6,1 ~ 8,0 | ≤8 | ≤2.0 |
| > 8,0 | ≤6 | ≤1.5 |
Physica, mechanica et dielectric proprietatibus
| No. | Proprietatibus | Unitas | Vexillum pretii | Typical valorem | ||
| 1 | Densitas | G / CM3 | 1.70 ~ 1.95 | 1.9 | ||
| 2 | Flacalis Fortitudo perpendicularis laminations (Longe) | Ad normalis conditio | MPA | ≥400 | DXL | |
| CLXXX ℃ +/- II ℃ | ≥200 | CD | ||||
| 3 | Impact fortitudinem (Charypy, SCARIFATIO, longum) | KJ / M2 | ≥37 | 50 | ||
| 4 | Adhesive / Vinculum Fortitudo | N | ≥5000 | (VI) CM | ||
| 5 | Aqua effusio | mg | Vide altera mensa | 11,8 | ||
| 6 | Nulla resistentia, parallela laminations | Ad normalis conditio | MΩ | ≥1.0 x CVI | 5.3 x CVII | |
| Postquam 24h | ≥1.0 x CII | 3,8 x CIV | ||||
| 7 | Dielectric dissipatio factor 1MHz | -- | ≤0.05 | 1.03 x 10-2 | ||
| 8 | Dielectric constans 1MHz | -- | ≤5.5 | 4.7 | ||
| 9 | Breakdown voltage, parallela laminations (per TRANSFERNGER ad XC ℃ +/- II ℃) | kV | ≥30 | 35 | ||
| 10 | Dielectric fortitudo, perpendicularis ad laminations (per TRANSFORMER ad XC ℃ +/- II ℃), 2mm sheet | MV / M | ≥11.8 | 18 | ||
Aqua effusio
| Mediocris crassitudine test samples (mm) | Aqua effusio (MG) | Mediocris crassitudine test samples (mm) | Aqua effusio (MG) | Mediocris crassitudine test samples (mm) | Aqua effusio (mg) |
| 0,5 | ≤17 | 2.5 | ≤21 | 12 | ≤38 |
| 0,8 | ≤18 | 3.0 | ≤22 | 16 | ≤46 |
| 1.0 | ≤18 | 5,0 | ≤25 | 20 | ≤52 |
| 1.6 | ≤19 | 8,0 | ≤31 | 25 | ≤61 |
| 2.0 | ≤20 | 10 | ≤34 | Vide dicta II | ≤73 |
| Remarks:I) Si calculata mediocris mensura crassitudine est inter duas crassitudine, de quibus in mensa, valores erit acquiritur per interpolationem. Si caculated mediocris mensurari crassitudine est minus 0.5mm, et vallibus non erit super 17mg. Si caculated mediocris mensuratur crassitudine est super 25mm, in valore non erit super 61mg.2), si nomini dente plus quam 25mm, erit machined ad 22.5mm in una parte. Machined latus sit lenis. | |||||
Stipare et repono
Sperdetur in loco ubi temperatus est altior quam XL ℃, et poni in cubiculo cubitorum altitudinis 50mm vel supra.
Custodiant ab igne, æstus (calefacere apparatus) et directe soles. Ptorage vitae laminas est XVIII mensibus a date de relinquens fabrica. Si repono durationem est super XVIII menses, quod productum et non potest esse post esse probata ut qualified.
Disputationes et cautiones application
A summus celeritate et parva secans profundum applicari cum machining propter laminas, infirma scelerisque conductivity.
Machining et cutting hoc productum et dimittere multum pulvis et fumigant. Apta mensuras esse capta ut pulveris gradus in gratum fines in operationibus. Locus exhaurit evacuatione et usura idoneam pulveris / particula personas sunt monuit.
Spermatibus subduntur umor postquam machined, coating insulating evanescere commendatur.